Abstract:
Polyethersulfone (PES)-expanded graphite nanocomposites have been prepared by solution blending route after sonicating expanded graphite in dichloromethane. It has been observed that ultrasonication results in nanosheets formation leading to a low percolation threshold of 3 wt.%. At 5 wt.% filler loading the conductivity is of the order of 10 2 S/cm. Hopping type of charge transport occurs at 3.2 wt.% expanded graphite in PES below which capacitive effects couple. The effective dielectric constant at low frequency increases with filler concentration. Impedance measurement has been carried out to eval- uate interfacial capacitance which, for 3.2 wt.% expanded graphite addition in PES, increases to 110 pF from 32 pF for 1 wt.% expanded graphite in the polymer. DSC analysis shows an increment of 12 C in the Tg of PES with 3 wt.% expanded graphite suggesting interaction between the polymer and filler.